Low temperature sintered ink for glass
- By screen printing or rolling coating, after sintering at 580-750℃ for 5-10 minutes, the colored glass coating with scratch resistance, acid and alkali resistance, bright color and high fullness is formed.
- Suitable for automotive, home appliances, architectural glass material, with better performance, more textured appearance.
- Various color effects can be prepared with different colors of inorganic color powder. With good performance and external feeling, super scratch resistance, scratch resistance, impact resistance.
General application method: screen printing
Screen printing - > Sintering 580-750℃*5-10Min
Paint film performance (PMMA material, PC material, UV surface)
Test item | Test method | Test result | property |
Film thickness | Film thickness | / | 15-25um |
Boiling resistance | Soak in 80 degree water bath for 30 minutes | No appearance change adhesion ≥4B | No appearance changes 5B |
Acid resistance | 0.1N H2SO4,80℃ | 72 hours,∆E<1 | No appearance changes 5B |
Alkali resistance | 10%NaOH, room temperature | 72 hours,∆E<1 | No scratch |
Solid content | 150 degrees x30 minutes | / | 79±4% |
Telephone: 0797-4216666 0752-3866668
Mail box: jxcicai@szcicai.cn
True transmission: 0797-4217188
Factory Address: Fine chemical Industry Park, Dingnan County, Ganzhou City, Jiangxi Province
R&d Center: No.23 Panli Road, Li Lin Town, Zhongkai High-tech Zone, Huizhou City, Guangdong Province